Zirconium beads can be used to polish many products, polishing zirconium beads generally with 1mm, 2mm, 3mm or more of the beads, can be polished wheels, hardware, medical equipment, jade, rings, necklaces and gold and silver jewelry, in the mirror polishing of the abrasive surface finish requirements are high, abrasive surface to be smooth, can not have grinding force, so that it will not scratch the work. Zirconium beads and polishing liquid are vibrated together in the roller barrel, which can throw the jewelry very bright, eliminating the manual polishing procedure, saving time and effort.

Zirconia beads, the color of pearl white, smooth surface, in the ceramic ball is a very hard abrasive, long use time, durable. Zirconia ceramic grinding medium is often used for ultrafine grinding of heavy calcium carbonate, kaolin, mica and other non-metallic minerals.

Parameter description

Zirconia content: 95%
Bulk gravity: 3.6g/cm3
Density: 6.1g/cm3
Vickers Hardness: 1250
Color: Pure white
Surface: bright
Size: 0.05mm, 0.1mm, 0.2mm-20mm

Cerium stabilized zirconia beads referred to as cerium zirconia beads, generally yellow, brown, black, relatively high density, widely used for grinding high viscosity materials, such as paint, ink, coatings, adhesives, paper, metal, non-metallic minerals and rare earth materials grinding and dispersion.

BZS
General Character

Ball-tec® BZS is produced by two different melting and sintering method, is a grinding media of the high performance and low cost.

BZA

General Character

Ball-tec® BZA is the most cost-effective ceramic grinding media , Made of modified zirconia powder. It is main use in mine industry.

BZY is a grinding media of the highest quality that meet with customers’ needs. use of yttria stabilized zirconia powder by hydrothermal method.
General Character

Feature & Application
High density and hardness
High wear-resistance and no contamination

BCZ

General Character

Ball-tec® BCZ is a grinding media of the highest density that meets with customers’ needs. Made by cerium stabilized zirconium oxide powder.